Very high cycle fatigue strength and crack growth of thin steel sheets
OUARABI, Mohand
Laboratoire Energétique Mécanique Electromagnétisme [LEME]
Université Paris Nanterre [UPN]
Laboratoire Energétique Mécanique Electromagnétisme [LEME]
Université Paris Nanterre [UPN]
PEREZ MORA, Ruben
Université Paris Nanterre [UPN]
Laboratoire Energétique Mécanique Electromagnétisme [LEME]
Université Paris Nanterre [UPN]
Laboratoire Energétique Mécanique Electromagnétisme [LEME]
BATHIAS, Claude
Université Paris Nanterre [UPN]
Laboratoire Energétique Mécanique Electromagnétisme [LEME]
See more >
Université Paris Nanterre [UPN]
Laboratoire Energétique Mécanique Electromagnétisme [LEME]
OUARABI, Mohand
Laboratoire Energétique Mécanique Electromagnétisme [LEME]
Université Paris Nanterre [UPN]
Laboratoire Energétique Mécanique Electromagnétisme [LEME]
Université Paris Nanterre [UPN]
PEREZ MORA, Ruben
Université Paris Nanterre [UPN]
Laboratoire Energétique Mécanique Electromagnétisme [LEME]
Université Paris Nanterre [UPN]
Laboratoire Energétique Mécanique Electromagnétisme [LEME]
BATHIAS, Claude
Université Paris Nanterre [UPN]
Laboratoire Energétique Mécanique Electromagnétisme [LEME]
< Reduce
Université Paris Nanterre [UPN]
Laboratoire Energétique Mécanique Electromagnétisme [LEME]
Language
en
Article de revue
This item was published in
Frattura ed Integrità Strutturale / Fracture and Structural Integrity. 2016-03-22, vol. 10, n° 36, p. 112-118
Università di Cassino
English Abstract
For basic observations or for industrial applications it is of interest to use flat specimens at very high frequency in the gigacycle regime. In this work, thin flat sheet, with 1.2 mm thickness of a complex phase ...Read more >
For basic observations or for industrial applications it is of interest to use flat specimens at very high frequency in the gigacycle regime. In this work, thin flat sheet, with 1.2 mm thickness of a complex phase ferrite-martensitic steels were considered for carrying out fatigue tests at high frequency (20 kHz) up to the gigacycle regime (>109 cycles). The crack initiation tests were carried out with water cooling, while the crack growth test were carried out in laboratory air at room temperature. All the tests were carried out under loading ratio R=-1. To do that, special designs of specimens were made and computed using FEM for defining the stress amplitude for endurance tests. Special attachments for specimens to the ultrasonic system’s horn were enhanced. A particular FEM computing of the stress intensity range on crack growth specimens was carried out for determining the specimen dimensions and an equation that defines the stress intensity range as a function of the harmonic displacement amplitude, dynamic Young’s modulus, material density and crack length. Detailed procedures and fatigue results are presented in this paper.Read less <
English Keywords
Fatigue resistance
Plate steel fatigue
Ultrasonic fatigue
Fatigue crack growth