Fabrication of artificial defects to study internal fatigue crack propagation in metals
Idioma
en
Article de revue
Este ítem está publicado en
Scripta Materialia. 2019, vol. 171, p. 87-91
Elsevier
Resumen
Fatigue specimens designed with controlled internal defects were obtained by diffusion bonding of Ti-6Al-4V sheets containing femtosecond laser drilled notches. Crack initiation from the internal defect occurred systematically. ...Leer más >
Fatigue specimens designed with controlled internal defects were obtained by diffusion bonding of Ti-6Al-4V sheets containing femtosecond laser drilled notches. Crack initiation from the internal defect occurred systematically. The cracks were characterised by in situ synchrotron X-ray tomography. Propagation rates are lower than those of surface cracks of comparable sizes in the same material and fall between experimental data obtained for fatigue cracks propagating in air and in vacuum.< Leer menos
Resumen en inglés
Fatigue specimens designed with controlled internal defects were obtained by diffusion bonding of Ti-6Al-4V sheets containing femtosecond laser drilled notches. Crack initiation from the internal defect occurred systematically. ...Leer más >
Fatigue specimens designed with controlled internal defects were obtained by diffusion bonding of Ti-6Al-4V sheets containing femtosecond laser drilled notches. Crack initiation from the internal defect occurred systematically. The cracks were characterised by in situ synchrotron X-ray tomography. Propagation rates are lower than those of surface cracks of comparable sizes in the same material and fall between experimental data obtained for fatigue cracks propagating in air and in vacuum. © 2019 Acta Materialia Inc.< Leer menos
Palabras clave en inglés
Titanium alloys
Ternary alloys
Synchrotrons
Synchrotron radiation
Spark plasma sintering
Fatigue of materials
Fatigue crack propagation
Aluminum alloys
Surface cracks
Propagation rate
Fatigue specimen
In-situ synchrotrons
Internal defects
Artificial defects
Fatigue cracks
Tomography
Vanadium alloys
Three-dimensional tomography
Orígen
Importado de HalCentros de investigación