PAN, Xiangnan; XU, Shouwen; QIAN, Guian; NIKITIN, Alexander; SHANYAVSKIY, Andrey; PALIN LUC, Thierry; HONG, Youshi

doi:10.1016/j.msea.2020.140110

Metadatos

Mostrar el registro completo del ítem

Licencia de uso del documento

PAN, Xiangnan
Chinese Academy of Sciences [Beijing] [CAS]

XU, Shouwen
Chinese Academy of Sciences [Beijing] [CAS]

QIAN, Guian
Chinese Academy of Sciences [Beijing] [CAS]

Idioma

Article de revue

Este ítem está publicado en

Materials Science and Engineering: A. 2020-11, vol. 798, p. 1-14

Elsevier

Resumen en inglés

Traditionally, equiaxed alpha grains rather than lamellar microstructure (LM) domains in titanium alloys are regarded as potential internal crack origins in high-cycle fatigue (HCF) and very-high-cycle fatigue (VHCF) re-gimes. Here, we found that the fatigue crack is prone to initiate from a large LM domain in a titanium alloy with the composition of LM and equiaxed microstructure (EM) of fine alpha grains. Then, the mechanisms of internal crack initiation and early growth for the cases of HCF and VHCF under stress ratio R =-1, 0.1 and 0.5 were addressed and a mechanism chart was constructed to illustrate the internal cracking behavior, especially showing that the numerous cyclic pressing process dominates the related microstructure evolution with grain size refinement and nanograin formation underneath the fracture surfaces in the region of crack initiation and early growth.< Leer menos

Palabras clave en inglés

Titanium alloy

Crack initiation

Facet

Very-high-cycle fatigue

Lamellar microstructure

Metadatos

Compartir este ítem

Licencia de uso del documento

The mechanism of internal fatigue-crack initiation and early growth in a titanium alloy with lamellar and equiaxed microstructure

Idioma

Este ítem está publicado en

Resumen en inglés

Palabras clave en inglés

URI

DOI

Orígen

Centros de investigación