Etude structurale et électrochimique d'oxydes de manganèse
Thèses de doctorat
Ce document a été publié dans
Date de soutenance
1997-10-02Résumé
LiMnO2 material was obtained with "chimie douce" reactions. This phase was utilized as positive electrode for lithium batteries. A study of their structural and electrochemical properties during de-intercalation, was ...Lire la suite >
LiMnO2 material was obtained with "chimie douce" reactions. This phase was utilized as positive electrode for lithium batteries. A study of their structural and electrochemical properties during de-intercalation, was performed. Otherwise, vanadium doped manganese oxides, Mn1-pVpO2 (p <= 0,05), were synthetized. Their crystalline structure was studied. It is very close to B-MnO2 manganese dioxide one. Those materials are promising positive electrode materials for lithium batteries with liquid electrolyte.< Réduire
La phase LiMnO2 a été obtenue par chimie douce. Ce matériau a été utilisé comme électrode positive dans des batteries au lithium. Une étude de l'évolution des propriétés structurales et électrochimiques lors de la ...Lire la suite >
La phase LiMnO2 a été obtenue par chimie douce. Ce matériau a été utilisé comme électrode positive dans des batteries au lithium. Une étude de l'évolution des propriétés structurales et électrochimiques lors de la désintercalation du lithium a été effectuée. Par ailleurs, les oxydes de manganèse dopés Mn1-pVpO2 (p <= 0,05) ont été préparés. Leur structure cristalline a été étudiée. Elle est très proche de celle du dioxide de manganèse B-MnO2. Ces matériaux présentent des performances électrochimiques prometteuses dans des batteries lithium à électrolyte liquide.< Réduire