Amorphous Polymers’ Foaming and Blends with Organic Foaming-Aid Structured Additives in Supercritical CO2, a Way to Fabricate Porous Polymers from Macro to Nano Porosities in Batch or Continuous Processes
HAURAT, Margaux
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
DUMON, Michel
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
HAURAT, Margaux
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
DUMON, Michel
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
< Réduire
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
Langue
EN
Article de revue
Ce document a été publié dans
Molecules. 2020-11-14, vol. 25, n° 22, p. 5320
Résumé en anglais
Organic polymers can be made porous via continuous or discontinuous expansion processes in scCO2. The resulting foams properties are controlled by the interplay of three groups of parameters: (i) Chemical, (ii) physico-chemical, ...Lire la suite >
Organic polymers can be made porous via continuous or discontinuous expansion processes in scCO2. The resulting foams properties are controlled by the interplay of three groups of parameters: (i) Chemical, (ii) physico-chemical, and (iii) technological/process that are explained in this paper. The advantages and drawbacks of continuous (extrusion, injection foaming) or discontinuous (batch foaming) foaming processes in scCO2, will be discussed in this article; especially for micro or nano cellular polymers. Indeed, a challenge is to reduce both specific mass (e.g., ρ < 100 kg·m−3) and cell size (e.g., average pore diameter ϕaveragepores < 100 nm). Then a particular system where small “objects” (coreshells CS, block copolymer MAM) are perfectly dispersed at a micrometric to nanometric scale in poly(methyl methacrylate) (PMMA) will be presented. Such “additives”, considered as foaming aids, are aimed at “regulating” the foaming and lowering the pore size and/or density of PMMA based foams. Differences between these additives will be shown. Finally, in a PMMA/20 wt% MAM blend, via a quasi one-step batch foaming, a “porous to nonporous” transition is observed in thick samples. A lower limit of pore size (around 50 nm) seems to arise.< Réduire