ARIF, Muhamad Fatikul; SAINTIER, Nicolas; MERAGHNI, Fodil; FITOUSSI, Joseph; CHEMISKY, Yves; ROBERT, Gilles

doi:10.1016/j.compositesb.2014.01.019

Métadonnées

Afficher la notice complète

Licence d’utilisation du document

ARIF, Muhamad Fatikul
Laboratoire d'Etude des Microstructures et de Mécanique des Matériaux [LEM3]

SAINTIER, Nicolas

MERAGHNI, Fodil
Laboratoire d'Etude des Microstructures et de Mécanique des Matériaux [LEM3]

Langue

Article de revue

Ce document a été publié dans

Composites Part B: Engineering. 2014-01-18, vol. 61, p. 55-65

Elsevier

Résumé en anglais

This paper aims at studying fatigue damage behavior of injection molded 30 wt% short glass fiber reinforced polyamide-66 composite (PA66/GF30). The evolution of dynamic modulus, hysteresis area, cyclic creep and temperature during fatigue tests were analyzed and discussed. Damage analyses by X-ray micro-computed tomography (lCT) technique on interrupted fatigue tests at several percentages of total fatigue life were performed to further understand the damage mechanisms and evolution during fatigue loading. It can be observed that experimental results related to the evolution of dynamic modulus, strain, temperature and energy dissipation are important and consistently complement each other for damage evaluation of PA66/GF30. During fatigue loading, diffuse damage occurs over the entire specimen though the damage does not necessarily exhibit the same level between different locations inside the specimen. The lCT analysis of voids characteristics demonstrates that the damage continuously increases during fatigue loading. The damage is developed notably along fiber interface in the form of fiber/matrix interfacial debonding.< Réduire

Mots clés en anglais

Polymer-matrix composites (PMCs)

Fatigue

Microstructures

Injection molding

Métadonnées

Partager cette publication !

Licence d’utilisation du document

Multiscale fatigue damage characterization in short glass fiber reinforced polyamide-66