Scaling invariance of fatigue crack growth in gigacycle loading regime
Langue
en
Article de revue
Ce document a été publié dans
Tech. Phys. Lett. 2010-11, vol. 36, n° 11, p. 1061-1063
Résumé en anglais
The role of the collective behavior of defect ensembles at the crack tip and the laws of fatigue crack propagation in R4 high-strength steel have been studied under conditions of symmetric tension-compression gigacycle ...Lire la suite >
Mots clés en anglais
very high cycle fatigue
scaling invariance
crack growth
metal
defects