LI, Yajie; YANG, Haicun; AHMADI, Azita; OMARI, Aziz; PU, Hongting

doi:10.1016/j.polymer.2022.125027

Métadonnées

Afficher la notice complète

Licence d’utilisation du document

LI, Yajie
Institut de Mécanique et d'Ingénierie [I2M]

YANG, Haicun

AHMADI, Azita
Institut de Mécanique et d'Ingénierie [I2M]

Langue

Article de revue

Ce document a été publié dans

Polymer. 2022-06-22, vol. 253

Résumé en anglais

Multilayer separators are widely used due to their wide shutdown window by combining lower melting temperature and higher melting temperature of different layers. With the development of high power lithium-ion batteries, multilayer separators equipped with effective thermal stability and flame retardancy are highly required. Herein, the poly(methyl methacrylate) modified attapulgite (ATPM) is selected as the heat resistant reinforcing component and blended with polypropylene (PP)/polyethylene (PE) respectively. Then we prepare PP(ATPM)/PE(ATPM) separators via multilayer coextrusion efficiently without multiple stretching processes, which can avoid serious separator shrinkage at elevated temperature. The intertwined ATPM could not only enhance the separator integrity, but also produce water vapor and oxide anti-flaming isolation layers at high temperatures. The as-prepared separators, referred to as MC-TIPS PP/PE/ATPM, exhibit higher thermal stability (with negligible dimensional shrinkage up to 180 °C), better flame retardancy and wider shutdown temperature window (124–183 °C) than the commercial multilayer separators. Moreover, the introduction of ester and hydroxyl groups could improve the wettability and electrolyte uptake of the separators. These properties, as well as the potential for large-scale production of multilayer coextrusion, make MC-TIPS PP/PE/ATPM an ideal choice for high-power battery separators.< Réduire

Mots clés en anglais

Attapulgite

Flame retardancy

Lithium-ion battery

Multilayer separators

Thermal stability

Métadonnées

Partager cette publication !

Licence d’utilisation du document

A thermal resistant and flame retardant separator reinforced by attapulgite for lithium-ion batteries via multilayer coextrusion