Influence of V2O5 on the magnetic properties of nickel–zinc–copper ferrites
Language
en
Article de revue
This item was published in
Journal of Magnetism and Magnetic Materials. 2007, vol. 312, n° 2, p. 328-330
Elsevier
English Abstract
Additions of V2O5 were used to decrease the sintering temperature and to enhance the densification of NiZnCu ferrite. With a small amount of V2O5 (0.6–1.2 wt%) as a sintering aid, densification at low sintering temperature ...Read more >
Additions of V2O5 were used to decrease the sintering temperature and to enhance the densification of NiZnCu ferrite. With a small amount of V2O5 (0.6–1.2 wt%) as a sintering aid, densification at low sintering temperature was observed. EDS analyses showed the presence of vanadium inside the ferrite grains. Microstructure investigation revealed heterogeneous grain size...Read less <