Synthesis and magnetic properties of the ternary germanide TbScGe
Language
en
Article de revue
This item was published in
Journal of Alloys and Compounds. 2013, vol. 560, p. 195-199
Elsevier
English Abstract
TbScGe is obtained as pure phase after melting of the constituents followed by an annealing at 1173 K. Contrary to what was suggested previously, this ternary germanide does not present a high temperature form with the ...Read more >
TbScGe is obtained as pure phase after melting of the constituents followed by an annealing at 1173 K. Contrary to what was suggested previously, this ternary germanide does not present a high temperature form with the hexagonal Ti5Ga4-type structure after melting and quenching; the as quenched sample is a mixture based on the two solid solutions (Tb1−xScx)5Ge3 and Tb1−xScx. TbScGe adopts the tetragonal CeScSi-type structure with a = 4.219 and c = 15.452 Å as unit cell parameters. Its investigation by magnetization and specific heat measurements reveals a ferromagnetic behavior below TC = 250 K inducing a moderate magnetocaloric effect; for a magnetic field change of 2 T, the magnetic entropy change ΔSm is equal to −1.6 J K−1 kg−1 which corresponds to an adiabatic temperature change ΔTad of 1.25 K.Read less <
English Keywords
Structural properties
Synthesis
Ternary germanide
Ferromagnetism
Magnetocaloric properties