Polystyrene-block-poly(ethylene oxide) stars as surface films at the air/water interface
TATON, Daniel
Laboratoire de Chimie des polymères organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
< Réduire
Laboratoire de Chimie des polymères organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
Langue
en
Article de revue
Ce document a été publié dans
Langmuir. 2005, vol. 21, n° 16, p. 7380-7389
American Chemical Society
Résumé en anglais
Star diblock copolymers containing polystyrene (PS) and poly(ethylene oxide) (PEO) were investigated as surface films at the air/water interface. Both classic and dendritic-like stars were prepared containing either a PS ...Lire la suite >
Star diblock copolymers containing polystyrene (PS) and poly(ethylene oxide) (PEO) were investigated as surface films at the air/water interface. Both classic and dendritic-like stars were prepared containing either a PS core and PEO corona or the reverse. The investigated polymers, consisting of systematic variations in architectures and compositions, were spread at the air/water interface, generating reproducible surface pressure-area isotherms. All of the films could be compressed to higher pressures than would be possible for pure PEO. For stars containing 20% or more PEO, three distinct regions appeared. At higher areas, the PEO absorbs in pancakelike structures at the interface with PS globules sitting atop. Upon compression, a pseudoplateau transition region appeared. Both regions strongly depended on PEO composition. The pancake area and the pseudoplateau width and pressure increased in a linear fashion with an increasing amount of PEO. In addition, minimum limits of PEO chain length and mass percentage were determined for observing a pseudoplateau. At small areas, the film proved less compressible, producing a rigid film in which PS dominated. Here, the film area increased with both molecular weight and the amount of PS. Comparison with pure linear PS showed the stars spread more, occupying greater areas. Among the stars, the PEO-core stars were more compact while the PS-core stars spread more. The influence of architecture in terms of the core/corona polymers and branching were also examined. The effects of architecture were subtle, proving less important than PEO chain length or mass percentage.< Réduire
Mots clés en anglais
POLYMERS
MORPHOLOGY
BEHAVIOR
COMPRESSION
AIR-WATER-INTERFACE
DIBLOCK COPOLYMER MONOLAYERS
PI-A ISOTHERMS
POLY(ETHYLENE OXIDE)
AGGREGATION
COLLAPSE
Origine
Importé de halUnités de recherche