Supramolecular Structure Characterization of Cellulose II Nanowhiskers Produced by Acid Hydrolysis of Cellulose I Substrates
SÈBE, Gilles
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 2 LCPO : Biopolymers & Bio-sourced Polymers
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 2 LCPO : Biopolymers & Bio-sourced Polymers
HAM-PICHAVANT, Frédérique
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 2 LCPO : Biopolymers & Bio-sourced Polymers
Leer más >
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 2 LCPO : Biopolymers & Bio-sourced Polymers
SÈBE, Gilles
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 2 LCPO : Biopolymers & Bio-sourced Polymers
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 2 LCPO : Biopolymers & Bio-sourced Polymers
HAM-PICHAVANT, Frédérique
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 2 LCPO : Biopolymers & Bio-sourced Polymers
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 2 LCPO : Biopolymers & Bio-sourced Polymers
KOFFI, Akissi Lydie Chantal
Swiss Federal Laboratories for Materials Science and Technology [Dübendorf] [EMPA]
Swiss Federal Laboratories for Materials Science and Technology [Dübendorf] [EMPA]
TINGAUT, Philippe
Swiss Federal Laboratories for Materials Science and Technology [Dübendorf] [EMPA]
< Leer menos
Swiss Federal Laboratories for Materials Science and Technology [Dübendorf] [EMPA]
Idioma
en
Article de revue
Este ítem está publicado en
Biomacromolecules. 2012, vol. 13, n° 2, p. 570-578
American Chemical Society
Resumen en inglés
Cellulose II nanowhiskers (CNW-II) were produced by treatment of microcrystalline cellulose with sulfuric acid by both controlling the amount of H2SO4 introduced and the time of addition during the hydrolysis process. The ...Leer más >
Cellulose II nanowhiskers (CNW-II) were produced by treatment of microcrystalline cellulose with sulfuric acid by both controlling the amount of H2SO4 introduced and the time of addition during the hydrolysis process. The crystalline structure was confirmed by both XRD and C-13 CP-MAS NMR spectroscopy. When observed between crossed polarizers, the cellulose II suspension displayed flow birefringence and was stable for several months. The CNW-II nanowhiskers were significantly smaller than the cellulose I nanowhiskers (CNW-I) and had a rounded shape at the tip. The CNW-II average length and height were estimated by AFM to be 153 +/- 66 and 4.2 +/- 1.5 nm, respectively. An average width of 6.3 +/- 1.7 nm was found by TEM, suggesting a ribbon-shape morphology for these whiskers. The average dimensions of the CNW-II elementary crystallites were estimated from the XRD data, using Scherrer's equation. A tentative cross-sectional geometry consistent with both XRD and NMR data was then proposed and compared with the geometry of the CNW-I nanowhiskers< Leer menos
Palabras clave en inglés
POLYMORPHS
C-13 NMR
MICROCRYSTALLINE CELLULOSE
ELECTRON-MICROSCOPY
NATIVE CELLULOSE
NANOCRYSTALS
NANOCOMPOSITES
DIFFRACTION
WHISKERS
FIBERS