POULON-QUINTIN, Angeline; ROUZÉ L’ALZIT, François; OGDEN, Emma; LARGE, Axel; BERTRAND, Caroline; BARTALA, Michel

doi:10.17352/2394-8418.000115

Metadatos

Mostrar el registro completo del ítem

Licencia de uso del documento

POULON-QUINTIN, Angeline
Institut de Chimie de la Matière Condensée de Bordeaux [ICMCB]

ROUZÉ L’ALZIT, François
Institut de Chimie de la Matière Condensée de Bordeaux [ICMCB]

OGDEN, Emma
Institut de Chimie de la Matière Condensée de Bordeaux [ICMCB]

Idioma

Article de revue

Este ítem está publicado en

Journal of Dental Problems and Solutions. 2022, vol. 9, n° 2, p. 035-041

Resumen en inglés

Recommendations to obtain the best bonding to silica-based ceramics are to prepare its surface by hydrofluoric-acid HF etching and regular application of a silane. This study investigated how the HF-etching followed by ultrasonic water bath cleaning or by an additional phosphoric acid treatment impacts the adhesion properties of a resin (G-CEM LinkForce®) with a lithium disilicate glass-ceramic (IPS Emax Press, Ivoclar Vivadent). Comparison is based on results obtained with HF etching and direct silane application. After HF-etching, a water ultrasonic bath (4 minutes), and a final air drying, the scratch test critical load increases (+ 46%) thanks to chemical bonding. Additional tests are presented including heat treatments (at 85 °C before and after silanization). If HF-etching is followed by phosphoric acid treatment and drying of silane at 85 °C, scratch test critical load increases (+ 42%) due to mechanical bonding. Similar adhesion properties are obtained with two opposite protocols.< Leer menos

Metadatos

Licencia de uso del documento

Chemical surface modification of lithium disilicate needles of a silica-based ceramic after HF-etching and ultrasonic bath cleaning: impact on the chemical bonding with silane