Towards a better understanding of the high-temperature oxidation of MAX phase Cr2AlC
Idioma
EN
Article de revue
Este ítem está publicado en
Journal of the European Ceramic Society. 2022-05, vol. 42, n° 5, p. 2089-2096
Resumen en inglés
High-temperature oxidation of bulk single crystal, fine and coarse grained polycrystals of Cr2AlC has been performed from 800 °C to 1500 °C. In the temperature range T = [800;1400] °C, an α-Al2O3 scale with a Cr7C3 subscale ...Leer más >
High-temperature oxidation of bulk single crystal, fine and coarse grained polycrystals of Cr2AlC has been performed from 800 °C to 1500 °C. In the temperature range T = [800;1400] °C, an α-Al2O3 scale with a Cr7C3 subscale are in-situ formed independently of the initial microstructure on top of the bulk Cr2AlC. CALPHAD calculations were performed to explain the formation of Cr7C3 instead of the expected mixture of carbides, indicating a favourable driving force for Cr7C3 formation. The kinetic study of the oxidation is consistent with previous works with an activation energy of about 400 kJ.mol−1. Oxidizing for a longer time (1000 h) or at higher temperature (1500 °C) leads to the formation of chromia in the former alumina scale, which correspond to the calculated equilibrium phases.< Leer menos
Palabras clave en inglés
CrAlC
High-temperature oxidation
Microstructure
Single crystal
Thermodynamic calculations
Proyecto ANR
Poitiers Graduate School on physico-chemical properties of INTerfaces for AeRonautic, Energy and Environment - ANR-18-EURE-0010
Centros de investigación