RIVERO, Clara; RICHARDSON, Kathleen; STEGEMAN, Robert; STEGEMAN, George; CARDINAL, Thierry; FARGIN, Evelyne; COUZI, Michel

Metadatos

Licencia de uso del documento

RIVERO, Clara
Institut de Chimie de la Matière Condensée de Bordeaux [ICMCB]
The College of Optics and Photonics [Orlando] [CREOL]

RICHARDSON, Kathleen
The College of Optics and Photonics [Orlando] [CREOL]
School of Material Science and Engineering

STEGEMAN, Robert
The College of Optics and Photonics [Orlando] [CREOL]

Idioma

Article de revue

Este ítem está publicado en

Glass Technology - European Journal of Glass Science and Technology Part A. 2005, vol. 46, n° 2, p. 80-84

Society of Glass Technology

Resumen en inglés

New glasses which exhibit a broadband Raman spectral response have been prepared and characterised for their Raman cross section and gain performance. Results on three different glass compositions in the system [(100-x)NaPO3-xNa2B4O7]:TiO2/Nb2O5=1 are summarised. The impact on the Raman properties of changing the phosphorus to boron ratio while maintaining the TiO2/Nb2O5 molar ratio equal to one, was examined. Polarised spontaneous Raman measurements are presented, and a comparison between the experimentally obtained Raman gain coefficient and that predicted from spontaneous Raman cross section measurements is made. Results obtained show that these glasses exhibit similar or slightly higher Raman gain coefficients than that of SiO2, with a spectral bandwidth almost five times greater (sim1300 cm-1).< Leer menos

Palabras clave en inglés

Characterization

Preparation

Raman spectroscopy

Glasses