BARBIER, David; GERMAIN, Lionel; HAZOTTE, Alain; GOUNÉ, Mohamed; CHBIHI, Abdelahad

doi:10.1007/s10853-014-8596-2

Metadatos

Mostrar el registro completo del ítem

Licencia de uso del documento

BARBIER, David
ArcelorMittal Maizières Research SA

GERMAIN, Lionel
Laboratoire d'Etude des Microstructures et de Mécanique des Matériaux [LEM3]
Labex DAMAS

HAZOTTE, Alain
Laboratoire d'Etude des Microstructures et de Mécanique des Matériaux [LEM3]
Labex DAMAS

Idioma

Article de revue

Este ítem está publicado en

Journal of Materials Science. 2015, vol. 50, n° 1, p. 374-381

Springer Verlag

Resumen en inglés

The present work investigates the interactions between ferrite recrystallization and austenite formation in dual-phase steels by experiments performed at high heating rate (100 °C/s). It was shown that both ferrite recrystallization and austenite formation are strongly coupled and interdependent. The kinetics of ferrite recrystallization is strongly affected by the formation of austenite and can be even inhibited in some cases. The microstructure is more heterogeneous and anisotropic when both the austenite formation and the ferrite recrystallization overlap. It was highlighted that the degree of anisotropy depends on the volume fraction of austenite at a given temperature. Furthermore, an unusual behavior for austenite growth was highlighted. It is characterized by a much higher volume fraction than those obtained under OrthoEquilibrium and ParaEquilibrium. The results, especially those at 715 °C close to the eutectoid plateau, at which the driving force for austenite growth is classically low, suggest a diffusionless transformation for austenite< Leer menos

DOI

http://dx.doi.org/10.1007/s10853-014-8596-2

Proyecto ANR

Design des Alliages Métalliques pour Allègement des Structures - ANR-11-LABX-0008

Orígen

Importado de Hal

Centros de investigación

Institut de Chimie de la Matière Condensée de Bordeaux (ICMCB) - UMR 5026