The praseodymium nickelate PrNiO3-δ was recently identified as one of the decomposition products of Pr2NiO4+δ oxygen electrode, raising the question of the role of this perovskite compound on the Pr2NiO4+δ performance and ageing behaviour. Herein, the electrochemical properties of PrNiO3-δ as cathode for Solid Oxide Fuel Cells (SOFCs) is reported. PrNiO3-δ, synthesized from the citrate-nitrate route, cristallizes in an orthorhombic structure (S.G.: Pnma). Under air, a transition to high temperature rhombohedral structure (S.G.: R-3c) occurs at around 600 °C, while its oxygen vacancy amount increases from δ 0.05 at room temperature up to 0.10 at high temperature. Thermal gravimetry analysis (TGA) measurements coupled with X-ray diffraction (XRD) characterizations show that above 1000 °C, in air, PrNiO3-δ starts to decompose into Pr2NiO4+δ and NiO through an intermediate transformation into Pr4Ni3O10+δ. The value of the polarization resistance (Rp) of co-sintered GDC-PrNiO3-δ electrode, at 950 °C in air for 2 h, is 0.91 Ω cm2 at 600 °C under air. It remains much higher than that of co-sintered GDC-Pr2NiO4+δ electrode (Rp = 0.15 Ω cm2), which means that the perovskite does not play any significant role in the electrochemical performance during long term operation of the Pr2NiO4+δ electrode< Leer menos