MOHANTY, Prachi; MARIK, Sourav; CHENNABASAPPA, Madhu; SINGH, D.; TOULEMONDE, Olivier; SINGH, Ravi P.

doi:10.1088/1361-6463/ab399e

Metadatos

Licencia de uso del documento

MOHANTY, Prachi
Indian Institute of Science Education and Research Bhopal [IISER Bhopal]

MARIK, Sourav
Laboratoire de cristallographie et sciences des matériaux [CRISMAT]
Institut de Chimie de la Matière Condensée de Bordeaux [ICMCB]

CHENNABASAPPA, Madhu
Siddaganga Institute of Technology
Institut de Chimie de la Matière Condensée de Bordeaux [ICMCB]

Idioma

Article de revue

Este ítem está publicado en

Journal of Physics D: Applied Physics. 2019, vol. 52, n° 47, p. 475001 (6 p.)

IOP Publishing

Resumen en inglés

We report the structural, magnetic, exchange bias, and magnetotransport effect in Sr4Fe3CoO11. The material crystallizes in the orthorhombic Cmmm space group. It shows antiferromagnetic (G-type) transition (TN = 255 K), along with interesting temperature-induced magnetization reversal (TComp. = 47 K measured at 100 Oe). The magnetic reversal can be elucidated considering the increased magnetocrystalline anisotropy with Co substitution. Magnetoresistance measurements show an interesting crossover from the negative to positive side at ∼100 K. The negative magnetoresistance reaches 80% at 25 K in 7 T magnetic field. Giant exchange bias effect is observed below TN under field cooling condition. The origin of the negative magnetoresistance and giant exchange bias in this sample can be attributed to the magnetic frustration.< Leer menos

Palabras clave en inglés

Compensated ferrimagnet

Giant exchange bias

Magnetization reversal

Metadatos

Licencia de uso del documento

Magnetization reversal, giant exchange bias effect and magnetoresistance in oxygen vacancy ordered Sr4Fe3CoO11