CHEN, Yung-Ta; CHANG, Yao-Jen; MURAKAMI, Hideyuki; GORSSE, Stéphane; YEH, An-Chou

doi:10.1016/j.scriptamat.2020.06.002

Metadatos

Mostrar el registro completo del ítem

Licencia de uso del documento

CHEN, Yung-Ta
Department of Materials Science and Engineering
National Institute for Materials Science [NIMS]

CHANG, Yao-Jen
Department of Materials Science and Engineering
High Entropy Materials Center

MURAKAMI, Hideyuki
National Institute for Materials Science [NIMS]
Department of Nanoscience and Nanoengineering

Idioma

Article de revue

Este ítem está publicado en

Scripta Materialia. 2020-10, vol. 187, p. 177-182

Elsevier

Resumen en inglés

In the context of cast alloy development for high temperature applications, high entropy superalloys (HESA) have exhibited superior cost specific tensile strength than that of superalloys such as CM247LC. Compositions of HESA are distinctively different from those of cast superalloys with higher contents of Fe and Ti, making HESA cheaper and lighter. Comparing to superalloys, although HESA has adopted the template of FCC-structured (γ) matrix and coherent L12-structured (γ′) precipitates, γ′ is enriched with solutes with higher intrinsic strength, rendering positive lattice misfit, and the high entropy γ matrix may have attributed to a good combination of strength and ductility.< Leer menos

Metadatos

Licencia de uso del documento

Designing high entropy superalloys for elevated temperature application