MARTIN, Lucile; MARTINEZ, Hervé; POINOT, Delphine; PECQUENARD, Brigitte; LE CRAS, Frédéric

doi:10.1021/jp3119633

Metadatos

Licencia de uso del documento

MARTIN, Lucile
Laboratoire d'Innovation pour les Technologies des Energies Nouvelles et les nanomatériaux [LITEN]
Institut pluridisciplinaire de recherche sur l'environnement et les matériaux [IPREM]

MARTINEZ, Hervé
Institut pluridisciplinaire de recherche sur l'environnement et les matériaux [IPREM]

POINOT, Delphine
Laboratoire d'Innovation pour les Technologies des Energies Nouvelles et les nanomatériaux [LITEN]
Institut de Chimie de la Matière Condensée de Bordeaux [ICMCB]

Idioma

Article de revue

Este ítem está publicado en

Journal of Physical Chemistry C. 2013, vol. 117, n° 9, p. 4421-4430

American Chemical Society

Resumen en inglés

The course of the conversion reaction during the electrochemical insertion/deinsertion of lithium in CuO thin film electrodes was surveyed by cyclic voltammetry (CV) and X-ray photoelectron spectroscopy (XPS). The electrochemical processes were studied through the comprehensive acquisition and interpretation of XPS and Auger spectra (Cu 2p, O 1s, Cu LMM) recorded at different stages of the first cycle of a Li/CuO cell. The reduction process consisting of three main steps leads successively to Cu+ and Cu0 and involves a Li2O2 peroxide type phase as an intermediate, whereas Li2O is the main lithiated oxide at the end of the discharge. Only the two last steps appear reversible in charge. No evidence of Cu2+ was found at the end of the charge at 3.5 V/Li+/Li, showing the irreversibility of the first step in our experimental conditions. Complementary XPS depth profile analyses were performed to check the evolution of the active material composition over the thickness of the electrode.< Leer menos

Palabras clave en inglés

X-ray Photoelectron Spectroscopy

Electrode

Thin films

Copper compounds

Metadatos

Licencia de uso del documento

Comprehensive X-ray photoelectron spectroscopy study of the conversion reaction mechanism of CuO in lithiated thin film electrodes

Idioma

Este ítem está publicado en

Resumen en inglés

Palabras clave en inglés

DOI

Orígen

Centros de investigación