Caractérisation structurale d'hydroxydes doubles lamellaires contenant des anions oxométallates (Mo, w) ou acrylate intercalés.
dc.contributor.author | VAYSSE, Christophe | |
dc.date | 2001-12-14 | |
dc.date.accessioned | 2021-01-13T14:04:40Z | |
dc.date.available | 2021-01-13T14:04:40Z | |
dc.identifier.uri | https://oskar-bordeaux.fr/handle/20.500.12278/25739 | |
dc.description.abstract | De nouveaux hydroxydes doubles lamellaires (LDHs) contenant des entités oxométallates (Mo,W) intercalées ont été préparés et caractérisés par diffraction des rayons X (DRX),analyse chimique,spectroscopie infrarouge (IR)et EXAFS.Dans les deux cas,des anions M2O72- (M =Mo,W) constitués de deux tétraèdres à sommet commun, sont intercalés. L'évolution structurale des phases LDHs contenant des ions oxométallates libres dans l'espace interfeuillet, traitées thermiquement jusqu'à 800°C, a été étudiée. Il a ainsi été montré que les anions oxométallates se greffent à deux feuillets adjacents au voisinage de 200°C. Le comportement thermique de phases contenant des anions carbonate intercalés a également été appréhendé par DRX in et ex situ, spectroscopie IR,analyse chimique et thermogravimétrie couplée à la spectrométrie de masse. Il a été mis en évidence un mono-greffage des anions carbonate aux feuillets. L'intercalation et l'oligomérisation d'anions acrylate dans les LDHs ont également été réalisées. Des différences de comportement sont observées selon la nature de l'ion substituant du nickel (Fe,Co ou Mn) dans les feuillets. Dans le cas du fer,la phase contenant les monomères intercalés a pu être isolée et caractérisée, alors que dans le cas du cobalt et du manganèse, une polymérisation spontanée, simultanément à l'intercalation dans la matrice, a été observée. Les macromolécules polymérisées in situ ont été extraites par échange anionique, dérivatisées en poly(acrylate de méthyle) et analysées par chromatographie d'exclusion stérique. | |
dc.description.abstractEn | New layered double hydroxides (LDHs),containing intercalated oxometalate species (Mo,W) were prepared and characterised by X-Ray Diffraction (XRD), chemical analysis, infrared spectroscopy (IR) and EXAFS. In both cases, M2O72- anions (M =Mo,W), made of corner-sharing tetrahedra, are intercalated. The structural evolution of LDHs containing free oxometalate species, thermally treated up to 800°C, was studied, showing that the oxometalate anions are grafted to two adjacent slabs at 200°C. The thermal behaviour of carbonate-intercalated LDHs was also studied by in and ex situ XRD, IR spectroscopy, chemical analysis and thermogravimetry, coupled with mass spectrometry. A mono-grafting of the carbonate anions to the slabs was shown. The intercalation and oligomerisation of acrylate anions into LDHs were also performed. Different behaviour are observed, depending on the substituting metal ion for nickel (Fe,Co or Mn) within the slab. In the case of iron, the monomer-intercalated phase could be isolated and characterised, while in the case of cobalt and manganese, a spontaneous polymerisation occurs, simultaneously to the intercalation. The macromolecules, polymerised in situ, were extracted by anionic exchange reaction, derivatised into poly(méthyl acrylate), and analysed by size exclusion chromatography. | |
dc.format | application/pdf | |
dc.language | fr | |
dc.rights | free | |
dc.subject | Physico-Chimie de la Matière Condensée | |
dc.subject | hydroxyde double lamellaire | |
dc.subject | hydrotalcite | |
dc.subject | chimie douce | |
dc.subject | intercalation | |
dc.subject | oxométallate | |
dc.subject | greffage | |
dc.subject | EXAFS | |
dc.subject | acrylate | |
dc.subject | polymérisation interfeuillet | |
dc.subject | matériaux hybrides organiques-inorganiques | |
dc.title | Caractérisation structurale d'hydroxydes doubles lamellaires contenant des anions oxométallates (Mo, w) ou acrylate intercalés. | |
dc.type | Thèses de doctorat | |
bordeaux.hal.laboratories | Thèses Bordeaux 1 Ori-Oai | * |
bordeaux.institution | Université de Bordeaux | |
bordeaux.COinS | ctx_ver=Z39.88-2004&rft_val_fmt=info:ofi/fmt:kev:mtx:journal&rft.title=Caract%C3%A9risation%20structurale%20d'hydroxydes%20doubles%20lamellaires%20contenant%20des%20anions%20oxom%C3%A9tallates%20(Mo,%20w)%20ou%20acrylate%20intercal%C3%A9s.&rft.atitle=Caract%C3%A9risation%20structurale%20d'hydroxydes%20doubles%20lamellaires%20contenant%20des%20anions%20oxom%C3%A9tallates%20(Mo,%20w)%20ou%20acrylate%20intercal%C3%A9s.&rft.au=VAYSSE,%20Christophe&rft.genre=unknown |