Génération de second harmonique dans des verres Borophosphate de Sodium et Niobium par polarisation thermique

Abstract

Second Harmonic Generation in polarized vitreous materials should permit the development of new electro-optic devices compatible with silica glass fiber. This thesis presents the results obtained on thermally poled glasses with compositions ((1-x)0.95 NaPO3 + 0.05Na2B4O7)+ x Nb2O5 (x < or = 0.5). A second order optical nonlinearity better than 4 pm/V has been induced in both bulk and thin films glasses. Characterization of materials before and after polarization and especially the description of the local structure of the glass network allowed to propose some mechanisms to describe the thermal poling treatment in such conductive glasses.

La génération de second harmonique induite par des traitements de polarisation dans des matériaux vitreux pourrait permettre le développement de nouveaux systèmes électrooptiques compatible avec les fibres optiques de silice. Dans ce contexte, cette thèse présente les résultats obtenus par polarisation thermique des verres ((1-x) 0.95 NaPO3 + 0.05Na2B4O7)+ x Nb2O5 (x < ou = 0.5). Une non linéarité optique d'ordre deux supérieure à 4pm/V a pu être induite à la fois dans le verre massif et le verre déposé sous forme de couche mince. L'analyse du verre avant et après polarisation et notamment de la structure locale du réseau vitreux permet une meilleure approche des processus mis en jeu lors du traitement dans des verres à aussi forte concentration en sodium et donc aussi conducteurs.