[K<sub>2</sub>Mn<sub>5</sub>{Mo(CN)<sub>7</sub>}<sub>3</sub>]: an open framework magnet with four Tc conversions orchestrated by guests and thermal history
Langue
en
Article de revue
Ce document a été publié dans
New Journal of Chemistry. 2011, vol. 35, n° 6, p. 1211-1218
Royal Society of Chemistry
Résumé en anglais
The 3D metal organic framework of formula [K<sub>2</sub>(H<sub>2</sub>O)<sub>4</sub>Mn<sub>5</sub>(H<sub>2</sub>O)<sub>8</sub>(MeCN){Mo(CN)<sub>7</sub>}<sub>3</sub>]*2H<sub>2</sub>O, 1a, gives rise to four ferri-magnets ...Lire la suite >
The 3D metal organic framework of formula [K<sub>2</sub>(H<sub>2</sub>O)<sub>4</sub>Mn<sub>5</sub>(H<sub>2</sub>O)<sub>8</sub>(MeCN){Mo(CN)<sub>7</sub>}<sub>3</sub>]*2H<sub>2</sub>O, 1a, gives rise to four ferri-magnets with distinct sets of attributes attained by controlled and sequential variation of its sorption state and a structural transition. 1a is prepared by solution (H<sub>2</sub>O) chemistry at ambient conditions by assembling the heptacyanomolybdate building unit {Mo(CN)<sub>7</sub>}<sup>4−</sup> with Mn(II) in the presence of MeCN. The resulting open-framework is achieved only with the small cyanide ligand that also ensures noteworthy magnetic performances. Its potential porosity (28% of solvent accessible volume) is sufficient to observe fast and efficient sorption processes that permit converting the attributes (<i>T</i><sub>c</sub> and <i>H</i><sub>c</sub>) of the corresponding magnets. It is shown that the magnetic ordering temperature <i>T</i><sub>c</sub> increases from 61 K (for 1a) to 82 K after solvent release whereas this <i>T</i><sub>c</sub> is 72 K upon the structural transition taking place for the guest-free magnet. A fourth magnet with <i>T</i><sub>c</sub> = 61 K is generated by H<sub>2</sub>O uptake. Concomitantly the coercive fields <i>H</i><sub>c</sub> vary between 70 and 1770 Oe. These processes, including the structural phase transition, are reversible by means of basic levers, <i>i.e.</i> thermal processing and H<sub>2</sub>O sorption, allowing inter-conversion among three of the four magnets. The crystal structure analysis for 1a, the XRPD for 1b, 1c, and 1d, the magnetic behavior for the four magnets, and TGA data are reported.< Réduire
Origine
Importé de halUnités de recherche