ALGA, M.; AMMAR, Abdelaziz; TANOUTI, B.; OUTZOURHIT, A.; MAUVY, Fabrice; DECOURT, Rodolphe

doi:10.1016/j.jssc.2005.06.030

Métadonnées

Afficher la notice complète

Licence d’utilisation du document

ALGA, M.
Laboratoire de Chimie des Matériaux Solides

AMMAR, Abdelaziz
Laboratoire de Chimie des Matériaux Solides

TANOUTI, B.
Laboratoire de Chimie des Matériaux Solides

Langue

Article de revue

Ce document a été publié dans

Journal of Solid State Chemistry. 2005, vol. vol. 178, n° 9, p. p. 2873-2879

Elsevier

Résumé en anglais

Doping Bi4V1.8Cu0.2O10.7 with niobium has led to the formation of the Bi4V1.8Cu0.2−xNbxO10.7+3x/2 solid solution. X-ray diffraction and thermal analysis have shown that only the compound with x=0.05 presents a tetragonal symmetry with a γ′ polymorph while the other compositions are of β polymorph. The influence of sintering temperature on the microstructure of the samples was investigated by the scanning electron microscopy (SEM). The ceramics sintered at temperatures higher than 820 °C present micro-craks. The evolution of the electrical conductivity with temperature and the degree of substitution has been investigated by impedance spectroscopy. Among all compositions studied the sample with x=0.05 presents the highest value of the conductivity.< Réduire

Mots clés en anglais

Aurivillius phases

Ionic conductors

BIMEVOX materials

Solid electrolyte

Métadonnées

Licence d’utilisation du document

Effect of Niobium doping on structural, thermal, sintering and electrical properties of Bi4V1.8Cu0.2O10.7