Show simple item record

dc.contributor.advisorCramail, Henri
dc.contributor.advisorGrelier, Stéphane
dc.contributor.authorSAVONNET, Etienne
dc.contributor.otherCramail, Henri
dc.contributor.otherGrelier, Stéphane
dc.contributor.otherTournilhac, François
dc.contributor.otherCoqueret, Xavier
dc.contributor.otherGérard, Jean-François
dc.contributor.otherVantorre-Defoort, Brigitte
dc.contributor.otherGrau, Etienne
dc.date2018-02-16
dc.identifier.urihttp://www.theses.fr/2018BORD0022/abes
dc.identifier.uri
dc.identifier.urihttps://tel.archives-ouvertes.fr/tel-03143731
dc.identifier.nnt2018BORD0022
dc.description.abstractLa grande majorité des résines époxy utilisées aujourd’hui sont issues ou dérivées du bisphénol-A (BPA). Cependant, le BPA est soumis à de très fortes régulations, notamment vis-à-vis de sa récente classification comme substance chimique extrêmement préoccupante par l’agence européenne des produits chimiques (ECHA). Dans un but d’anticiper les évolutions de régulation, ArianeGroup a décidé de remplacer cette substance chimique de ces formulations. Ces travaux de thèse portent donc sur l’élaboration de nouvelles résines époxy biosourcées ayant des propriétés similaires voire supérieures aux références dérivées du bisphénol-A. Pour cela, une bioplatforme de monomères polyépoxydés issus de la vanilline, du méthyl vanillate, du 2,6-diméthoxyphénol et de l’eugénol a été développée. Ces précurseurs biosourcés ont ensuite été utilisés comme précurseurs de réseaux époxyde par réticulation avec des amines. Les réseaux réticulés biosourcés ainsi obtenus ont démontré des propriétés thermomécaniques remarquables bien supérieures à la référence de type DGEBA, notamment en termes de température de transition vitreuse (>300 °C) et taux de coke (>50%). En parallèle de ces travaux, la synthèse de diamines biosourcées, dérivées de la divanilline, et pouvant être utilisées comme agents de réticulation de résines époxy, a été réalisée. Des réseaux époxyde entièrement biosourcés ont ainsi été synthétisés et présentent des propriétés thermomécaniques prometteuses.
dc.description.abstractEnToday, most of the epoxy resins produced are derived from bisphenol-A (BPA). However, BPA is subject to strong regulations, particularly because of its recent classification as chemical of very high concern by the European Chemicals Agency (ECHA). In order to anticipate new regulations, ArianeGroup has decided to replace this substance in its applications. The aim of this thesis is to develop new bio-based epoxy thermosets with comparable thermomechanical properties as the ones issued from bisphenol-A-based materials. For this purpose, a bio-platform of epoxy monomers from vanillin, methyl vanillate, 2,6-dimethoxyphenol and eugenol was developed. These precursors were cross-linked with amines used as curing agent to obtain bio-based epoxy networks. The latter demonstrated thermomechanical properties well above the DGEBA-type reference, especially in terms of glass transition temperature (> 300 °C) and char content (> 50%). Finally, the synthesis of bio-based diamines derived from divanillin was developed and enabled the synthesis of fully bio-based epoxy networks with promising thermomechanical properties.
dc.language.isoen
dc.subjectBisphénol-A
dc.subjectDGEBA
dc.subjectRésines époxy
dc.subjectRéseaux époxyde biosourcés
dc.subjectDivanilline
dc.subjectPolyaddition
dc.subjectTransition vitreuse
dc.subjectTaux de coke
dc.subject.enBisphenol A
dc.subject.enDGEBA
dc.subject.enEpoxy resins
dc.subject.enBio-based epoxy thermosets
dc.subject.enDivanillin
dc.subject.enPolyaddition
dc.subject.enGlass transition temperature
dc.subject.enChar content
dc.titleDéveloppement de réseaux époxydes biosourcés pour lanceurs aérospatiaux
dc.title.enDevelopment of bio-based epoxy thermosets for aerospace launchers
dc.typeThèses de doctorat
dc.contributor.jurypresidentTournilhac, François
bordeaux.hal.laboratoriesLaboratoire de Chimie des Polymères Organiques (Bordeaux)
bordeaux.type.institutionBordeaux
bordeaux.thesis.disciplinePolymères
bordeaux.ecole.doctoraleÉcole doctorale des sciences chimiques (Talence, Gironde)
star.origin.linkhttps://www.theses.fr/2018BORD0022
dc.contributor.rapporteurCoqueret, Xavier
dc.contributor.rapporteurGérard, Jean-François
bordeaux.COinSctx_ver=Z39.88-2004&rft_val_fmt=info:ofi/fmt:kev:mtx:journal&rft.title=D%C3%A9veloppement%20de%20r%C3%A9seaux%20%C3%A9poxydes%20biosourc%C3%A9s%20pour%20lanceurs%20a%C3%A9rospatiaux&rft.atitle=D%C3%A9veloppement%20de%20r%C3%A9seaux%20%C3%A9poxydes%20biosourc%C3%A9s%20pour%20lanceurs%20a%C3%A9rospatiaux&rft.au=SAVONNET,%20Etienne&rft.genre=unknown


Files in this item

FilesSizeFormatView

There are no files associated with this item.

This item appears in the following Collection(s)

Show simple item record