EL MAY, Mohamed; MAY, Mohamed; SAINTIER, Nicolas; PALIN LUC, Thierry; DEVOS, Olivier; BRUCELLE, Olivier

doi:10.1016/j.corsci.2018.01.034

Metadatos

Mostrar el registro completo del ítem

Licencia de uso del documento

Idioma

Article de revue

Este ítem está publicado en

Corrosion Science. 2018, vol. 133, p. 397-405

Elsevier

Resumen en inglés

This paper presents an analytical model for assessing the corrosion fatigue crack initiation life on a martensitic stainless steel X12CrNiMoV12-3 in high cycle fatigue regime (between 105 and 107 cycles). Based on in-situ electrochemical measurements during corrosion fatigue tests in NaCl aqueous solution, the corrosion fatigue crack initiation mechanism was identified. Two main stages were investigated: (i) the fracture of the passive film by slip bands and (ii) the free dissolution of the metal developing fatigue crack initiation from a critical corrosion defect. The depassivation stress threshold corresponds to the median fatigue strength at 107 cycles for fatigue corrosion tests. For an applied stress range less than this threshold, the depassivation phenomenon was not observed at 107 cycles and no crack initiation occurred. The proposed model takes into account the depassivation process induced by the slip bands emergence at the specimen surface and the corrosion rate under cyclic loading. The experimental results are compared to the proposed model taking into account mechanical and electrochemical material parameters.< Leer menos

Palabras clave en inglés

Modelling

Stainless steel

Corrosion fatigue

Pitting corrosion

Metadatos

Compartir este ítem

Licencia de uso del documento

Modelling of corrosion fatigue crack initiation on martensitic stainless steel in high cycle fatigue regime

Idioma

Este ítem está publicado en

Resumen en inglés

Palabras clave en inglés

URI

DOI

Orígen

Centros de investigación