One-shot synthesis of high molar mass polyurethane in supercritical carbon dioxide

dc.rights.licenseopen
hal.structure.identifierLaboratoire de Chimie des polymères organiques [LCPO]
dc.contributor.authorRENAULT, Benjamin
hal.structure.identifierLaboratoire de l'intégration, du matériau au système [IMS]
dc.contributor.authorTASSAING, Thierry
hal.structure.identifierLaboratoire de Chimie des polymères organiques [LCPO]
hal.structure.identifierTeam 4 LCPO : Polymer Materials for Electronic, Energy, Information and Communication Technologies
dc.contributor.authorCLOUTET, Eric
IDREF: 151048681
hal.structure.identifierLaboratoire de Chimie des polymères organiques [LCPO]
hal.structure.identifierTeam 2 LCPO : Biopolymers & Bio-sourced Polymers
dc.contributor.authorCRAMAIL, Henri
dc.date.accessioned2020
dc.date.available2020
dc.date.created2007
dc.date.issued2007
dc.identifier.issn0887-624X
dc.identifier.urihttps://oskar-bordeaux.fr/handle/20.500.12278/20827
dc.description.abstractEnWell-defined polyurethane-polydimethylsiloxane particles of tunable diameter in the range of 0.5-20 mu m were synthesized in "one-shot" by step-growth polymerization using supercritical carbon dioxide (scCO(2)) as a dispersant medium. Polymerizations were carried out at 60 degrees C and above 25 MPa, after the solubility of each reactant in scCO(2) has been determined in its typical reaction concentration. The synthesis of such copolymers was achieved by polyaddition between short aliphatic diols, that is, ethylene glycol, 1,4-butanediol (BD) or polyethylene oxide (M-n = 200 g mol(-1)), and tolylene-1,4-di-isocyanate (TDI) in the presence of mono or di-isocyanate-terminated polydimethylsiloxane (PDMS) as reactive stabilizers and dibutyltin dilaurate as a catalyst. The nature of the diol used as well as the functionality of the reactive stabilizer incorporated was found to have a dramatic effect on the molar mass and the morphology of the resulting product. Thus, copolymers obtained from the polyaddition of BD and TDI in the presence of di-isocyanate-terminated PDMS exhibit molar mass up to 90,000 g mol-1. Thermal behaviors of copolymers were also examined by differential scanning calorimetry. All samples exhibited only one glass transition temperature (T-g) and were found to be totally amorphous. A logical decrease of the T-g was observed as the length of the diol incorporated increased, that is, as the density of urethane linkages within the polymer decreased. (c) 2007 Wiley Periodicals, Inc.
dc.language.isoen
dc.publisherWiley
dc.subject.enCO2
dc.subject.enpolyurethanes
dc.subject.encore-shell polymers
dc.subject.ensurfactants
dc.title.enOne-shot synthesis of high molar mass polyurethane in supercritical carbon dioxide
dc.typeArticle de revue
dc.identifier.doi10.1002/pola.22313
dc.subject.halChimie/Polymères
bordeaux.journalJournal of Polymer Science Part A: Polymer Chemistry
bordeaux.page5649-5661
bordeaux.volume45
bordeaux.hal.laboratoriesLaboratoire de Chimie des Polymères Organiques (LCPO) - UMR 5629*
bordeaux.issue23
bordeaux.institutionBordeaux INP
bordeaux.institutionUniversité de Bordeaux
bordeaux.peerReviewedoui
hal.identifierhal-00279719
hal.version1
hal.origin.linkhttps://hal.archives-ouvertes.fr//hal-00279719v1
bordeaux.COinSctx_ver=Z39.88-2004&rft_val_fmt=info:ofi/fmt:kev:mtx:journal&rft.jtitle=Journal%20of%20Polymer%20Science%20Part%20A:%20Polymer%20Chemistry&rft.date=2007&rft.volume=45&rft.issue=23&rft.spage=5649-5661&rft.epage=5649-5661&rft.eissn=0887-624X&rft.issn=0887-624X&rft.au=RENAULT,%20Benjamin&TASSAING,%20Thierry&CLOUTET,%20Eric&CRAMAIL,%20Henri&rft.genre=article


Fichier(s) constituant ce document

FichiersTailleFormatVue

Il n'y a pas de fichiers associés à ce document.

Ce document figure dans la(les) collection(s) suivante(s)

Afficher la notice abrégée