Production, cellular structure and thermal conductivity of microcellular (methyl methacrylate) - (butyl acrylate) - (methyl methacrylate) triblock copolymers
DUMON, Michel
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
Leer más >
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
DUMON, Michel
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
< Leer menos
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
Idioma
en
Article de revue
Este ítem está publicado en
Polymer International. 2010, vol. 60, n° 1, p. 146-152
Wiley
Resumen en inglés
Microcellular foaming of a (methyl methacrylate)-(butyl acrylate)-(methyl methacrylate) triblock copolymer was carried out by means of supercritical CO2 in a single-step process. The experiments were performed at 40 degrees ...Leer más >
Microcellular foaming of a (methyl methacrylate)-(butyl acrylate)-(methyl methacrylate) triblock copolymer was carried out by means of supercritical CO2 in a single-step process. The experiments were performed at 40 degrees C using a pressure of 300 bar (30 MPa) during 24 h. The depressurization times were modified from 2 to 30 min, leading to cell sizes from 10 to 100 mu m, and relative densities from 0.11 to 0.17. It was found that the key parameter to control cell size and density was depressurization time: longer depressurization times generated larger cell sizes and lower densities. The thermal conductivity of these materials was measured using the transient plane source technique, and it was found that this decreased as the density was reduced. Various models for the prediction of thermal conductivity by conduction were tested. It was found that all the models underestimated the experimental results due to a significant contribution of radiation heat flow for these materials. (C) 2010 Society of Chemical Industry< Leer menos
Palabras clave en inglés
cellular structure
microcellular foams
thermal conductivity
triblock copolymers