Hyperbranched polyesters by polycondensation of fatty acid-based ABn-type monomers
GRAU, Etienne
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 2 LCPO : Biopolymers & Bio-sourced Polymers
Leer más >
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 2 LCPO : Biopolymers & Bio-sourced Polymers
GRAU, Etienne
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 2 LCPO : Biopolymers & Bio-sourced Polymers
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 2 LCPO : Biopolymers & Bio-sourced Polymers
TATON, Daniel
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 1 LCPO : Polymerization Catalyses & Engineering
CRAMAIL, Henri
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 2 LCPO : Biopolymers & Bio-sourced Polymers
< Leer menos
Laboratoire de Chimie des Polymères Organiques [LCPO]
Team 2 LCPO : Biopolymers & Bio-sourced Polymers
Idioma
en
Article de revue
Este ítem está publicado en
Green Chemistry. 2017
Royal Society of Chemistry
Resumen en inglés
Widely available vegetable oils were readily derivatized into chemically pure ABn-type monomers (n = 2 or 3). Their polymerization led to unprecedented hyperbranched polyesters. Four different AB2/AB3-type monomers bearing ...Leer más >
Widely available vegetable oils were readily derivatized into chemically pure ABn-type monomers (n = 2 or 3). Their polymerization led to unprecedented hyperbranched polyesters. Four different AB2/AB3-type monomers bearing one A-type methyl ester and two or three B-type alcohol functions were purposely synthesized via two elementary steps, i.e. epoxidation of the internal double bond of the vegetable oil precursors followed by ring-opening of the epoxy groups under acidic conditions. The polycondensation of these bio-sourced monomers was performed in bulk, in the presence of an appropriate catalyst, giving access to modular hyperbranched polyesters with tunable properties. Among the catalysts tested, zinc acetate, 1,5,7-triazabicyclo[4.4.0]dec-5-ene (TBD) and sodium methoxide proved the most effective, allowing the achievement of molar masses in the range 3000–10 000 g mol−1 and dispersities varying from 2 to 15, depending on the initial conditions. The degree of branching, DB, as determined by 1H NMR spectroscopy, was found to be between 0.07 and 0.45. The as-devised hyperbranched polyesters displayed either amorphous or semi-crystalline properties, as a function of the selected AB2/AB3-type initial monomers, with a glass transition temperature, Tg, ranging from −33 to 9 °C and a decomposition temperature at 5 wt% of the sample, Td5%, varying from 204 to 340 °C.< Leer menos
Palabras clave en inglés
HyperBranched polymers
polyester
bio-sourced