Low thermal conductivity of endogenous manganese silicide/Si composites for thermoelectricity
Idioma
en
Article de revue
Este ítem está publicado en
Materials Letters. 2015, vol. 155, p. 41-43
Elsevier
Resumen en inglés
Higher manganese silicide (HMS) based alloys with eutectic composition (Si-33.3 at% Mn) were prepared by arc-melting, melt-spinning and ball milling in order to evaluate the effect of microstructure on the thermal conductivity. ...Leer más >
Higher manganese silicide (HMS) based alloys with eutectic composition (Si-33.3 at% Mn) were prepared by arc-melting, melt-spinning and ball milling in order to evaluate the effect of microstructure on the thermal conductivity. Powder X-ray diffraction, SEM, EPMA and TEM analysis confirmed the presence of Si as a secondary phase distributed in the HMS matrix phase. Thermal properties of the samples were studied in the temperature range of 300–800 K. The microstructure refinement resulting from ball milling leads to a decrease of the thermal conductivity from 4.4 W/mK to 1.9 W/mK, whereas melt-spinning is inefficient to this respect. The results show an opportunity to produce bulk higher manganese silicide alloys with reduced thermal conductivity in order to enhance its thermoelectric performance.< Leer menos
Palabras clave en inglés
Higher manganese silicides
Spark plasma sintering
Hot uni-axial pressing
Thermoelectric properties
Mechanical alloying