An anhydrous high-pressure synthesis route to rutile type RhO2
Idioma
en
Article de revue
Este ítem está publicado en
Zeitschrift fur Naturforschung B. 2006, vol. 61, n° 12, p. 1500-1506
Verlag der Zeitschrift Fuer Naturforschung
Resumen en inglés
A new anhydrous high-pressure synthesis route was developed for rutile type RhO2. Rhodium(III) chloride was reacted with Na2O2 at 600 ◦C under an oxygen pressure of 200 MPa yielding RhO2 and NaCl. X-ray powder diffractometer ...Leer más >
A new anhydrous high-pressure synthesis route was developed for rutile type RhO2. Rhodium(III) chloride was reacted with Na2O2 at 600 ◦C under an oxygen pressure of 200 MPa yielding RhO2 and NaCl. X-ray powder diffractometer data and TEM observations confirmed the rutile structure: P42/mnm, a = 448.7(1), c = 308.9(1) pm, x(O) = 0.3125(8), leading to Rh–O distances of 195.0 (4×) and 198.3 pm (2×) in the slightly elongated octahedra. Structural transformations associated with the production of oxygen vacancies can be initiated by electron-beam heating.< Leer menos
Palabras clave en inglés
High-pressure
Synthesis
Crystal Chemistry
Orígen
Importado de HalCentros de investigación