HAJLAOUI, Thameur; HARNAGEA, Catalin; MICHAU, Dominique; JOSSE, Michaël; PIGNOLET, Alain

doi:10.1016/j.jallcom.2017.04.051

Metadatos

Mostrar el registro completo del ítem

Licencia de uso del documento

HAJLAOUI, Thameur
Institut National de la Recherche Scientifique [Québec] [INRS]

HARNAGEA, Catalin
Institut National de la Recherche Scientifique [Québec] [INRS]

MICHAU, Dominique
Institut de Chimie de la Matière Condensée de Bordeaux [ICMCB]

Idioma

Article de revue

Este ítem está publicado en

Journal of Alloys and Compounds. 2017, vol. 711, p. 480-487

Elsevier

Resumen en inglés

Multiferroic Ba2NdFeNb4O15-based composite thin films have been deposited on Pt/Si(100) substrates by pulsed laser deposition. Structural investigation demonstrated the achievement of highly c-oriented thin films of Ba2NdFeNb4O15 upon optimization. Macroscopic ferroelectric hysteresis loops showed that ferroelectric properties were considerably improved compared to those of the ceramic of the same composition. This improvement was related to the degree of c-orientation of the films, which was controlled via the growth conditions. The investigation of the films microelectromechanical properties confirmed that ferroelectricity was conserved down to the nanoscale. Furthermore, after an initial modest decrease of the polarization of less than 4% during the first 106 switching cycles, the films did not show any significant further fatigue up to 108 cycles. The presence of a magnetic secondary phase has been confirmed by measuring ferromagnetic hysteresis loops, demonstrating the achievement of ferroelectric-magnetic nanocomposite thin films based on tetragonal tungsten bronze Ba2NdFeNb4O15, which exhibit multiferroic properties at room temperature.< Leer menos

Palabras clave en inglés

Multiferroic

Thin film

Composite

Room temperature properties

Metadatos

Licencia de uso del documento

Highly oriented multiferroic Ba2NdFeNb4O15 -based composite thin films with tetragonal tungsten bronze structure on silicon substrates