Iron phosphate thin films have been obtained under controlled conditions by chemical conversion deposition. The films were formed on polycrystalline α-iron by immersion in acetone, as an organic solvent. After deposition, the films were investigated by x-ray photoelectron spectroscopy (XPS) and their influence on the thermal oxidation of α-iron was studied by means of in situ low incidence x-ray diffraction of synchrotron radiation. The study reveals interesting features related to the structure of both the phosphate and thermal oxide films. The XPS data suggest the iron phosphate to be constituted of long chains of phosphate groups PO^3-₄ these groups being interconnected by Fe²⁺and Fe³⁺ cations. X-ray diffraction measurements have shown a significant modification of the oxidation behavior of α-iron at 400 °C and atmospheric pressure, which is derived from the presence of the thin film: α- Fe₂&nbsp;O₃ formation is clearly enhanced to the detriment of Fe₃&nbsp;O₄ compared to the oxidation of pure iron in which Fe₃&nbsp;O₄ is the dominant phase. As the growth rate of the α- Fe₂ O₃ layer is significantly reduced compared to that of Fe₃&nbsp;O₄ thus the phosphated layers may find niche applications in low-to-moderate temperature environments.< Leer menos