ALLAIN, Sébastien Y.P.; GAUDEZ, Steve; GEANDIER, Guillaume; DANOIX, Frédéric; SOLER, Michel; GOUNÉ, Mohamed

doi:10.1016/j.scriptamat.2020.02.022

Métadonnées

Afficher la notice complète

Licence d’utilisation du document

ALLAIN, Sébastien Y.P.
Institut Jean Lamour [IJL]

GAUDEZ, Steve
Institut Jean Lamour [IJL]

GEANDIER, Guillaume
Labex DAMAS
Institut Jean Lamour [IJL]

Langue

Article de revue

Ce document a été publié dans

Scripta Materialia. 2020-05, vol. 181, p. 108-114

Elsevier

Résumé en anglais

Based on the evolution of the positions and intensities of the diffraction peaks, high energy X-ray diffraction (HEXRD) is recognized as the ultimate method to follow quantitatively in situ phase transformations in steels. However, the possible asymmetricity of diffraction peaks is seldom considered, and is known to bear information. A procedure for quantifying their skewness is proposed. In the case of a third generation high strength steel obtained by quench and partitioning 1< Réduire

Mots clés en anglais

steel

martensite

austenite

partitioning

X-Ray diffraction

DOI

http://dx.doi.org/10.1016/j.scriptamat.2020.02.022

Project ANR

Partition du carbone dans les phases ferritiques nanostructurées: cinétiques et microstructures - ANR-14-CE07-0029
Design des Alliages Métalliques pour Allègement des Structures - ANR-11-LABX-0008