LASBRUGNAS, Carine; THOMAS, Philippe; MASSON, Olivier; CHAMPARNAUD-MESJARD, Jean-Claude; FARGIN, Evelyne; RODRIGUEZ, Vincent

Metadatos

Mostrar el registro completo del ítem

Licencia de uso del documento

LASBRUGNAS, Carine
Science des Procédés Céramiques et de Traitements de Surface [SPCTS]

THOMAS, Philippe
Axe 3 : organisation structurale multiéchelle des matériaux

MASSON, Olivier
Axe 3 : organisation structurale multiéchelle des matériaux

Idioma

Article de revue

Este ítem está publicado en

Glass Technology. 2005, vol. 46, n° 2, p. 71-75

Society of Glass Technology

Resumen en inglés

Second harmonic signals have been successfully generated in thermally poled 85%TeO2–15%WO3 glasses. Thermal poling of these glasses was undertaken at various temperatures and heating times using a voltage of 4·5 kV. The sample thickness was 500 mum. Second harmonic generation (SHG) in the poled glasses was analysed using the Maker fringes technique. After optimisation of the poling conditions (T=280°C, t=1 h), high chi(2) values (about 1·6 pm/V) were obtained. It was demonstrated that this thermal poling treatment has generated optically nonlinear zones on the anodic surface. The thickness of the surface layer given a SHG was thin (5·22 mum), as classically observed with tellurite glasses. The possible reorientation, under electric field, of the glass structural entities could be the origin of such second order nonlinear properties.< Leer menos

Palabras clave en inglés

Tellurite glasses

Second harmonic generation

Tungsten

Orígen

Importado de Hal

Centros de investigación

Institut de Chimie de la Matière Condensée de Bordeaux (ICMCB) - UMR 5026