TRAD, Khiem; CARLIER-LARREGARAY, Dany; CROGUENNEC, Laurence; WATTIAUX, Alain; BEN AMARA, Mongi; DELMAS, Claude

doi:10.1021/ic101130m

Metadatos

Mostrar el registro completo del ítem

Licencia de uso del documento

TRAD, Khiem
Institut de Chimie de la Matière Condensée de Bordeaux [ICMCB]

CARLIER-LARREGARAY, Dany
Institut de Chimie de la Matière Condensée de Bordeaux [ICMCB]

CROGUENNEC, Laurence
Institut de Chimie de la Matière Condensée de Bordeaux [ICMCB]

Idioma

Article de revue

Este ítem está publicado en

Inorganic Chemistry. 2010, vol. 49, n° 22, p. 10378-10389

American Chemical Society

Resumen en inglés

The alluaudite lithiated phases Li(0.5)Na(0.5)MnFe(2)(PO(4))(3) and Li(0.75)Na(0.25)MnFe(2)(PO(4))(3) were prepared via a sol-gel synthesis, leading to powders with spongy characteristics. The Rietveld refinement of the X-ray and neutron diffraction data coupled with ab initio calculations allowed us for the first time to accurately localize the lithium ions in the alluaudite structure. Actually, the lithium ions are localized in the A(1) and A(1)' sites of the tunnel. Mössbauer measurements showed the presence of some Fe(2+) that decreased with increasing Li content. Neutron diffraction revealed the presence of a partial Mn/Fe exchange between the two transition metal sites that shows clearly that the oxidation state of the element is fixed by the type of occupied site. The electrochemical properties of the two phases were studied as positive electrodes in lithium batteries in the 4.5-1.5 V potential window, but they exhibit smaller electrochemical reversible capacity compared with the non-lithiated NaMnFe(2)(PO(4))(3). The possibility of Na(+)/Li(+) ion deintercalation from (Na,Li)MnFe(2)(PO(4))(3) was also investigated by DFT+U calculations.< Leer menos

Metadatos

Licencia de uso del documento

Structural study of the Li(0.5)Na(0.5)MnFe2(PO4)3 and Li(0.75)Na(0.25)MnFe2(PO4)3 alluaudite phases and their electrochemical properties as positive electrodes in lithium batteries.

Idioma

Este ítem está publicado en

Resumen en inglés

DOI

Orígen

Centros de investigación