BOUKHRIS, Amal; HIDOURI, Mourad; GLORIEUX, Benoit; BEN AMARA, Mongi

doi:10.1016/S1002-0721(12)60369-X

Metadatos

Mostrar el registro completo del ítem

Licencia de uso del documento

BOUKHRIS, Amal
Matériaux Inorganiques

HIDOURI, Mourad
Matériaux Inorganiques

GLORIEUX, Benoit
Institut de Chimie de la Matière Condensée de Bordeaux [ICMCB]

Idioma

Article de revue

Este ítem está publicado en

Journal of Rare Earths. 2013, vol. 31, n° 9, p. 849-856

Elsevier

Resumen en inglés

Na2BaMg(PO4)2 was synthesized and characterized by X-ray diffraction, differential thermal analysis (DTA), 31P NMR spectroscopy and photoluminescence measurements. This compound crystallized in the PView the MathML sourcem1 space group of the trigonal system with the parameters of equivalent hexagonal cell a=0.5305(1) nm and c=0.6986(3) nm. The structure showed a perfect isotipysm with the mineral glaserite K3Na(SO4)2. Thus, it exhibited a lamellar framework which could be described as the stacking along the [001] direction of [MgP2O84−]∞ layers of corner sharing MgO6 polyhedra and PO4 tetrahedra. The Ba2+ cations were located within the interlayer space, while the Na+ ones were found in large cavities bound to the layers. The DTA analysis showed that this compound melt congruently at 1385 K. The 31P NMR spectrum was consistent with the presence of a single phosphorus site in the structure. Optical properties were investigated for the 5% doped Eu3+ and Eu2+ phases. The trivalent europium was used as a local probe, replacing barium while the divalent europium was used to examine whether this material could be used as an optical applications.< Leer menos

Palabras clave en inglés

Phosphate

31P NMR

Crystal structure

Europium

Photoluminescence

Rare earths

Metadatos

Licencia de uso del documento

Na2BaMg(PO4)2 : synthesis, crystal structure and europium photoluminescence properties