Tuning of the high temperature behaviour of Si–C–N ceramics via the chemical crosslinking of poly(vinylmethyl-co-methyl)silazanes with controlled borane contents
Language
EN
Article de revue
This item was published in
Open Ceramics. 2021, vol. 5, p. 100055
English Abstract
The thermal stability, elemental/phase composition evolution and crystallization behaviour of Si–B–C–N ceramics obtained by the pyrolysis of a series of poly (vinylmethyl-co-methyl)silazanes displaying various boron contents ...Read more >
The thermal stability, elemental/phase composition evolution and crystallization behaviour of Si–B–C–N ceramics obtained by the pyrolysis of a series of poly (vinylmethyl-co-methyl)silazanes displaying various boron contents were investigated through annealing in the temperature range 1000–1800 °C under nitrogen atmosphere. The increase of the boron content in the early stage of the process involved the nucleation of β-SiC, inhibited the crystallization of α-Si3N4 and modified the activity of the sp2-hybridised carbon phase in the derived ceramics obtained at 1000 and 1400 °C. At 1800 °C, low boron content Si–B–C–N ceramics gradually evolved toward a major SiC phase mainly formed via the carbothermal reaction of amorphous Si3N4 whereas high boron content Si–B–C–N ceramics led to highly stable materials with a complex microstructure made of SiC, Si3N4 and a BN-rich B(C)N phase that inhibited the activity of sp2-hybridised carbon toward the carbothermal reaction of amorphous Si3N4 and significantly reduced the SiC crystallization process.Read less <
English Keywords
Si–B–C–N
Polysilazanes
Boron
Polymer derived ceramics
Crystallization
Link to research data